Objectives: The aim of this study was to evaluate the morphological effects and the surface irregularities produced by different methods of mechanical stripping (abrasive strips and burs) and chemical stripping (37% orthophosphoric acid) and the surface changes following the finishing procedures (polishing strips) or the subsequent application of sealants, in order to establish the right stripping method that can guarantee the smoothest surface. We have also analysed the level of wear on the different abrasive strips employed, according to their structure. Materials and methods: 160 proximal surfaces of 80 sound molar teeth extracted for orthodontic and periodontal reasons, were divided into: 1 control group with non-treated enamel proximal surfaces and 5 different groups according to the stripping method used, were observed with scanning electron microscopy (SEM). Each one of the 5 treated groups was also divided into 3 different subgroups according to the finishing procedures or the subsequent application of sealants. Results: The finishing stage following the manual reduction proves to be fundamental in reducing the number and depth of grooves created by the stripping. After the air rotor stripping method, the use of sealants is advised in order to obtain a smoother surface. The analysis of the combinations of mechanical and chemical stripping showed unsatisfactory results. Concerning the wear of the strips, we have highlighted a different abrasion degree for the different types of strips analysed with SEM. Conclusions: The enamel damages are limited only if the finishing procedure is applied, independently of the type of abrasive strip employed. It would be advisable, though clinically seldom possible, the use of sealants after the air rotor stripping technique. Obiettivi: Lo scopo di questo studio è stato valutare gli effetti morfologici e le irregolarità di superficie prodotte da metodi differenti di stripping meccanico(strisce abrasive e frese) e stripping chimico(acido ortofosforico 37%) ed i cambiamenti di superficie conseguenti alle procedure di rifinitura (strisce 3M polishing) o di successiva applicazione di sigillanti. Tutto questo al fine di identificare la più corretta metodologia per lo stripping e garantire la presenza di superficie più liscia.Inoltre è stato analizzato il livello di usura delle differenti strisce abrasive utilizzate in accordo con la loro struttura. Materiali e metodi: Sono state analizzate160 superfici interprossimali di 80 malori integri estratti per motivi ortodontici o ragioni parodontali. Queste sono state divise in:-1 gruppo controllo con superfici prossimali non trattate;-5 gruppi differenti in accordo con il metodo di stripping usato.Tutti i gruppi sono stati analizzati con il microscopio elettronico a scansione(SEM).Ognuno dei 5 gruppi trattati è stato inoltre diviso in 3 differenti sottogruppi in accordo con le differenti procedure di stripping e la successiva applicazione di sigillanti. Risultati: La fase di rifinitura successiva alla riduzione interprossimale ha dimostrato di essere fondamentale per la riduzione del numero delle abrasioni profonde create con lo stripping. L'analisi delle combinazioni tra stripping meccanico e stripping chimico ha dimostrato risultati insoddisfacenti. Riguardo all'usura delle strisce abbiamo evidenziato un differente grado di abrasione delle differenti tipologie di strisce utilizzate e successivamente analizzate al SEM. Conclusioni: I danni allo smalto sono limitati solo se vieni effettuata la rifinitura, indipendentemente dal tipo di strisce impiegate. Sarebbe opportuno, sebbene sia clinicamente possibile raramente, l'uso di sigillanti dopo le procedure di stripping meccanico. Objectifs: Le but de cette étude est d'évaluer les effets morphologiques et les irrégularités de surface produites par de méthodes différentes de réduction par action mécanique (bandelettes abrasives et fraises dentaires) et stripping par action chimique (acide orthophosphorique à 37%). Il en va de même pour les changements de surface suite aux procédures de finition (bandes abrasives 3M polishing) ou bien suite à l'application successive de scellants, tout cela pour identifier la méthodologie la plus correcte pour le stripping et pour obtenir des surfaces plus lisses.Par surcroît, on a analysé le niveau d'usure des différentes bandes abrasives employées conformément à leur structure. Matériels et méthodes: On a analysé 160 surfaces interproximales de 80 molaires intègres extraites pour des motifs d'orthodontie ou bien pour des raisons parodontales. Ensuite, déclinaison en :-1 groupe de contrôle avec surfaces proximales non traitées.-5 groupes différents conformément à la méthode de réduction employée.Tous les groupes on été analysés au MEB (Microscope Electronique à balayage). Chacun des cinq groupes traités a été divisé en 3 différents sous-groupes, conformément aux différentes procédures de stripping et application successive de scellants. Résultats: La phase de finition après la réduction interproximale s'est avérée être fondamentale pour amenuiser le nombre d'abrasions profondes provoquées par le stripping. L'analyse des combinaisons entre stripping mécanique et stripping chimique a affiché des résultats insatisfaisants. Pour ce qui est de l'usure, nous avons montré un degré différent d'abrasion des différentes typologies de bandelettes employées et par la suite analysée au MEB. Conclusions: Les dégâts de l'émail ne sont limités que si l'on réalise la finition, indépendamment du type de bandelettes employées. Il serait opportun d'utiliser des scellants, bien que cliniquement il ne soit pas souvent possible, après les procédures de réduction mécanique. Objetivos: El fin de este estudio es valorar los efectos morfológicos y las irregularidades de superficie ocasionadas por métodos diferentes de tallado mecánico (tiras abrasivas y fresas) y stripping químico (ácido ortofosfórico al 37%), los cambios de superficie a raíz de los procesos de acabado (tiras 3M polishing) o bien aplicaciones sucesivas de sellantes. Lo anterior con el objeto de identificar la metodologías correcta para el stripping y obtener superficies más lisas.Además, se analizó el nivel de desgaste de las diferente tiras abrasivas de conformidad con su estructura. Materiales y métodos: Se analizaron 160 superficies interproxinmales de 80 molares íntegros extraídos por motivos ortodónticos o por razones periodontales. Se desglosaron en:-1 grupo de control con superficies proximales no tratadas.-5 grupos diferentes de acuerdo con el método de tallado utilizado.Todos los grupos fueron analizados con microscopio electrónico de barrido (SEM). Cada uno de los 5 grupos tratados se subdividió en 3 diferentes subgrupos de acuerdo con los procedimientos de stripping y la aplicación sucesiva de sellantes. Resultados: La fase de acabado después de la reducción interproximal resultó ser fundamental para disminuir el número de las abrasiones profundas ocasionadas con el strpping. El análisis de las combinaciones entre tallado mecánico y stripping químico arrojó resultados insatisfactorios Con respecto al desgaste de las tiras, destacamos un nivel distinto de abrasión de las diferentes tipologías de tiras empleadas y posteriormente analizadas con SEM. Conclusiones: Es posible limitar los daños del esmalte sólo si se aplica el proceso de acabado, con independencia del tipo de tiras empleadas. Sería oportuno utilizar sellantes, a pesar de que clthomampersan © 2010 Società Italiana di Ortodonzia SIDO.
Grippaudo, C., Cancellieri, D., Grecolini, M. E., Deli, R., Comparison between different interdental stripping methods and evaluation of abrasive strips: SEM analysis, <<PROGRESS IN ORTHODONTICS>>, 2010; 11 (2): 127-137. [doi:10.1016/j.pio.2010.08.001] [http://hdl.handle.net/10807/161893]
Comparison between different interdental stripping methods and evaluation of abrasive strips: SEM analysis
Grippaudo, Cristina
;Deli, Roberto
2010
Abstract
Objectives: The aim of this study was to evaluate the morphological effects and the surface irregularities produced by different methods of mechanical stripping (abrasive strips and burs) and chemical stripping (37% orthophosphoric acid) and the surface changes following the finishing procedures (polishing strips) or the subsequent application of sealants, in order to establish the right stripping method that can guarantee the smoothest surface. We have also analysed the level of wear on the different abrasive strips employed, according to their structure. Materials and methods: 160 proximal surfaces of 80 sound molar teeth extracted for orthodontic and periodontal reasons, were divided into: 1 control group with non-treated enamel proximal surfaces and 5 different groups according to the stripping method used, were observed with scanning electron microscopy (SEM). Each one of the 5 treated groups was also divided into 3 different subgroups according to the finishing procedures or the subsequent application of sealants. Results: The finishing stage following the manual reduction proves to be fundamental in reducing the number and depth of grooves created by the stripping. After the air rotor stripping method, the use of sealants is advised in order to obtain a smoother surface. The analysis of the combinations of mechanical and chemical stripping showed unsatisfactory results. Concerning the wear of the strips, we have highlighted a different abrasion degree for the different types of strips analysed with SEM. Conclusions: The enamel damages are limited only if the finishing procedure is applied, independently of the type of abrasive strip employed. It would be advisable, though clinically seldom possible, the use of sealants after the air rotor stripping technique. Obiettivi: Lo scopo di questo studio è stato valutare gli effetti morfologici e le irregolarità di superficie prodotte da metodi differenti di stripping meccanico(strisce abrasive e frese) e stripping chimico(acido ortofosforico 37%) ed i cambiamenti di superficie conseguenti alle procedure di rifinitura (strisce 3M polishing) o di successiva applicazione di sigillanti. Tutto questo al fine di identificare la più corretta metodologia per lo stripping e garantire la presenza di superficie più liscia.Inoltre è stato analizzato il livello di usura delle differenti strisce abrasive utilizzate in accordo con la loro struttura. Materiali e metodi: Sono state analizzate160 superfici interprossimali di 80 malori integri estratti per motivi ortodontici o ragioni parodontali. Queste sono state divise in:-1 gruppo controllo con superfici prossimali non trattate;-5 gruppi differenti in accordo con il metodo di stripping usato.Tutti i gruppi sono stati analizzati con il microscopio elettronico a scansione(SEM).Ognuno dei 5 gruppi trattati è stato inoltre diviso in 3 differenti sottogruppi in accordo con le differenti procedure di stripping e la successiva applicazione di sigillanti. Risultati: La fase di rifinitura successiva alla riduzione interprossimale ha dimostrato di essere fondamentale per la riduzione del numero delle abrasioni profonde create con lo stripping. L'analisi delle combinazioni tra stripping meccanico e stripping chimico ha dimostrato risultati insoddisfacenti. Riguardo all'usura delle strisce abbiamo evidenziato un differente grado di abrasione delle differenti tipologie di strisce utilizzate e successivamente analizzate al SEM. Conclusioni: I danni allo smalto sono limitati solo se vieni effettuata la rifinitura, indipendentemente dal tipo di strisce impiegate. Sarebbe opportuno, sebbene sia clinicamente possibile raramente, l'uso di sigillanti dopo le procedure di stripping meccanico. Objectifs: Le but de cette étude est d'évaluer les effets morphologiques et les irrégularités de surface produites par de méthodes différentes de réduction par action mécanique (bandelettes abrasives et fraises dentaires) et stripping par action chimique (acide orthophosphorique à 37%). Il en va de même pour les changements de surface suite aux procédures de finition (bandes abrasives 3M polishing) ou bien suite à l'application successive de scellants, tout cela pour identifier la méthodologie la plus correcte pour le stripping et pour obtenir des surfaces plus lisses.Par surcroît, on a analysé le niveau d'usure des différentes bandes abrasives employées conformément à leur structure. Matériels et méthodes: On a analysé 160 surfaces interproximales de 80 molaires intègres extraites pour des motifs d'orthodontie ou bien pour des raisons parodontales. Ensuite, déclinaison en :-1 groupe de contrôle avec surfaces proximales non traitées.-5 groupes différents conformément à la méthode de réduction employée.Tous les groupes on été analysés au MEB (Microscope Electronique à balayage). Chacun des cinq groupes traités a été divisé en 3 différents sous-groupes, conformément aux différentes procédures de stripping et application successive de scellants. Résultats: La phase de finition après la réduction interproximale s'est avérée être fondamentale pour amenuiser le nombre d'abrasions profondes provoquées par le stripping. L'analyse des combinaisons entre stripping mécanique et stripping chimique a affiché des résultats insatisfaisants. Pour ce qui est de l'usure, nous avons montré un degré différent d'abrasion des différentes typologies de bandelettes employées et par la suite analysée au MEB. Conclusions: Les dégâts de l'émail ne sont limités que si l'on réalise la finition, indépendamment du type de bandelettes employées. Il serait opportun d'utiliser des scellants, bien que cliniquement il ne soit pas souvent possible, après les procédures de réduction mécanique. Objetivos: El fin de este estudio es valorar los efectos morfológicos y las irregularidades de superficie ocasionadas por métodos diferentes de tallado mecánico (tiras abrasivas y fresas) y stripping químico (ácido ortofosfórico al 37%), los cambios de superficie a raíz de los procesos de acabado (tiras 3M polishing) o bien aplicaciones sucesivas de sellantes. Lo anterior con el objeto de identificar la metodologías correcta para el stripping y obtener superficies más lisas.Además, se analizó el nivel de desgaste de las diferente tiras abrasivas de conformidad con su estructura. Materiales y métodos: Se analizaron 160 superficies interproxinmales de 80 molares íntegros extraídos por motivos ortodónticos o por razones periodontales. Se desglosaron en:-1 grupo de control con superficies proximales no tratadas.-5 grupos diferentes de acuerdo con el método de tallado utilizado.Todos los grupos fueron analizados con microscopio electrónico de barrido (SEM). Cada uno de los 5 grupos tratados se subdividió en 3 diferentes subgrupos de acuerdo con los procedimientos de stripping y la aplicación sucesiva de sellantes. Resultados: La fase de acabado después de la reducción interproximal resultó ser fundamental para disminuir el número de las abrasiones profundas ocasionadas con el strpping. El análisis de las combinaciones entre tallado mecánico y stripping químico arrojó resultados insatisfactorios Con respecto al desgaste de las tiras, destacamos un nivel distinto de abrasión de las diferentes tipologías de tiras empleadas y posteriormente analizadas con SEM. Conclusiones: Es posible limitar los daños del esmalte sólo si se aplica el proceso de acabado, con independencia del tipo de tiras empleadas. Sería oportuno utilizar sellantes, a pesar de que clthomampersan © 2010 Società Italiana di Ortodonzia SIDO.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.